Aṣeṣe No.: HONYPLAS-PAI
Brand: Irufẹ Honyplas
Ta sipo | : | Kilogram |
Iru Apoti | : | Papa Package |
Awọn ohun elo Hayplas® Pai ni a tun mọ bi: polumamide-impnide. O tun ni awọn anfani. Iwọn otutu ti o funni laaye ni afẹfẹ jẹ ga ga (iṣẹ lilọsiwaju ni 250 ° C). Iwọn ti o dara julọ ni iwọn otutu ti 250 ℃, to dara julọ ikogun ati awọn ohun-ini ikọlu. Iyatọ UV resistance. Ti o tayọ si itankalẹ agbara rẹ (γ-egungun ati awọn x-egungun) ohun elo) ohun elo) awọn ohun elo ti a lo pupọ julọ, gẹgẹ bi awọn ohun elo ti ko ni paroncias, awọn edidi, ti ndagba awọn oruka ipin ati gbigbero awọn ẹya compressor. O jẹ ṣiṣu agbara giga pẹlu agbara ti o ga julọ ati rigirity laarin awọn igbona gbona ni 275 ° C (525 ° F). Ọja yii ni o ni agbara ijapa ọkọ oju-omi kekere, ati atako kero (pẹlu resistance si awọn oṣere ti o lagbara pupọ), ṣiṣe o dara pupọ fun awọn ohun elo ni awọn agbegbe awọn agbegbe lile. Agbara igba pipẹ ati lile ni awọn iwọn otutu to 275 ° ti o dara julọ iyara iyara alakikanju lati iwọn otutu to si 275 ° awọn ipo otutu to gaju. Sooro si awọn acids lagbara ati ọpọlọpọ awọn ẹya ara adayeda ina ti Ordertor. Alabọde kekere ti imugboroosi gbona
PAM Speed (poluyamide-imp) jẹ ohun elo ṣiṣu ti o lagbara pupọ ati lile. O ti wa ni igbagbogbo ni awọn agbegbe otutu otutu ga, awọn ohun-ini miiran yoo padanu awọn ohun-ini ẹrọ wọn ni tenpertitura gbona gbona. Le iduroṣinṣin ti o dara julọ ni 270 iwọn celsius.pai jẹ ohun elo iduroṣinṣin pupọ ti o jẹ ki o yan ohun elo ti o tayọ fun awọn ohun elo ti o nilo ẹrọ ifarada si ifarada. Pai Sutable ti a lo ninu sisẹ ẹrọ ẹrọ tabi iṣẹ akanṣe imọ-ẹrọ.
Isẹ iwọn otutu: 260-400
Awọ: Ayabaye, dudu, iresi ofeefee
Iwuwo: 1.40g / CM3 (iwuwo gangan ti wa ni ti a fiyesi i ikẹhin)
Ifarada: +/- 0.1-0.5mm, ni ibamu si awọn titobi oriṣiriṣi
Honyplas® Pai Awọn abuda:
1.Hoat-sooro: le ṣiṣẹ labẹ iwọn otutu ti o ga pupọ ni acek] ún
Iduroṣinṣin to apọju: le tọju iduroṣinṣin iwọn to pipe labẹ 250 ° C
Okun: Agbara giga rẹ jẹ ailopin ninu agbegbe ṣiṣu ti ko ni aabo ni bayi
4.Exclent Wiwo-resistance
5.Outting ultraviet r resisation resistance
Ipilẹ aropin
7.Ije idẹ kekere
8.Good vigidmity, irọrun, agbara alkaline
9.Good itanna ina
Igbasilẹ Honyplas® Pa Awọn ile-iṣẹ Ile-iṣẹ:
Awọn ohun elo idanwo, mimu iyara to gaju, ooru sooro awọn ẹrọ ohun elo, ẹrọ ounje, alurin ẹrọ gbigbẹ ati bẹbẹ lọ.
Honyplas® Pa awọn titobi wa:
0.5Mx0.5m 1Mx1m 1Mx2m 0mx2m tabi awọn ege kekere; Awọn titobi pataki le ge bi ibeere.
Sisanra: 1mm-100mm
Honyplas® Pa Imọ
Property | Test Method | Unit | High strength type | Wear resistance type | ||||||
4203L | 5030 | 7130 | 4301 | 4275 | 4435 | 4630 | 4645 | |||
Tensile strength | D638 | MPa | 152 | 221 | 221 | 113 | 117 | 94 | 81.4 | 114 |
Elongation at break | D638 | % | 7.6 | 2.3 | 1.5 | 3.3 | 2.6 | 1.0 | 1.9 | 0.8 |
Flexural strength | D790 | MPa | 282 | 374 | 310 |
|
200 |
|
|
|
23℃ | 244 | 338 | 355 | 219 | 212 | 152 | 131 | 154 | ||
135℃ | 174 | 251 | 263 | 165 | 157 | 129 |
|
|
||
232℃ | 120 | 184 | 177 | 113 | 111 | 91 |
|
|
||
Flexural modulus | D790 | GPa | 7.9 | 14.1 | 24.6 |
|
9.6 |
|
|
|
23℃ | 5.0 | 11.7 | 19.9 | 6.9 | 7.3 | 14.8 | 6.8 | 12.4 | ||
135℃ | 3.9 | 10.7 | 15.6 | 5.5 | 5.6 | 11.2 |
|
|
||
232℃ | 3.6 | 9.9 | 13.1 | 4.5 | 5.1 | 10.3 |
|
|
||
Shear strength | D732 | MPa | 128 | 140 | 120 | 112 | 77 | 60 |
|
85 |
Izod impact strength(3.2mm) | D256 | J/m |
|
|
|
|
|
|
|
|
Notched |
|
|
142 | 79 | 47 | 63 | 84 | 43 | 48 | 37 |
No notch |
|
|
1062 | 504 | 340 | 404 | 250 | 219 | 160 | 107 |
Distortion temperature(1.82MPa) | D648 | ℃ | 278 | 282 | 282 | 279 | 280 | 278 | 279 | 281 |
CLTE | D696 | ppm/℃ | 30.6 | 16.2 | 9.0 | 25.2 | 25.2 | 14.4 | 11.5 | 4.5 |
Flammability grade | UL94 |
|
94 V-0 | 94 V-0 | 94 V-0 | 94 V-0 | 94 V-0 | 94 V-0 |
|
|
Limit oxygen index | D2863 | % | 45 | 51 | 52 | 44 | 45 |
|
|
|
Volume resistivity | D257 | ohm-cm | 2x10^17 | 2x10^17 |
|
8 x 10^15 | 8 x 10^15 | 2 x 107 |
|
|
Density | D792 | g/cm3 | 1.42 | 1.61 | 1.48 | 1.46 | 1.51 | 1.59 | 1.56 | 1.56 |
Hardness(Rockwell E) | D785 |
|
86 | 94 | 94 | 72 | 70 | 62 |
|
|
Water absorption(24H) | D570 | % | 0.33 | 0.24 | 0.26 | 0.28 | 0.33 | 0.12 | 0.2 | 0.3 |
Gbólólólóhùn Asiri: Asiri rẹ ṣe pataki pupọ si wa. Ile-iṣẹ wa ṣe ileri lati ṣe sọ alaye ti ara ẹni si eyikeyi ifihan pẹlu awọn igbanilaaye rẹ.
Fọwọsi alaye diẹ sii ki o le wọle si ọ ni iyara
Gbólólólóhùn Asiri: Asiri rẹ ṣe pataki pupọ si wa. Ile-iṣẹ wa ṣe ileri lati ṣe sọ alaye ti ara ẹni si eyikeyi ifihan pẹlu awọn igbanilaaye rẹ.